C14181 Copper vs. C15500 Copper
Both C14181 copper and C15500 copper are copper alloys. Their average alloy composition is basically identical. There are 26 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C14181 copper and the bottom bar is C15500 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Elongation at Break, % | 15 | |
| 3.0 to 37 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 43 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 210 | |
| 280 to 550 |
| Tensile Strength: Yield (Proof), MPa | 130 | |
| 130 to 530 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 200 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1080 |
| Melting Onset (Solidus), °C | 1080 | |
| 1080 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 380 | |
| 350 |
| Thermal Expansion, µm/m-K | 17 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 33 |
| Density, g/cm3 | 9.0 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 2.7 |
| Embodied Energy, MJ/kg | 41 | |
| 42 |
| Embodied Water, L/kg | 310 | |
| 360 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 28 | |
| 15 to 84 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 69 | |
| 72 to 1210 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 6.5 | |
| 8.6 to 17 |
| Strength to Weight: Bending, points | 8.8 | |
| 11 to 17 |
| Thermal Diffusivity, mm2/s | 110 | |
| 100 |
| Thermal Shock Resistance, points | 7.4 | |
| 9.8 to 20 |
Alloy Composition
| Cadmium (Cd), % | 0 to 0.0020 | |
| 0 |
| Carbon (C), % | 0 to 0.0050 | |
| 0 |
| Copper (Cu), % | 99.9 to 100 | |
| 99.75 to 99.853 |
| Lead (Pb), % | 0 to 0.0020 | |
| 0 |
| Magnesium (Mg), % | 0 | |
| 0.080 to 0.13 |
| Phosphorus (P), % | 0 to 0.0020 | |
| 0.040 to 0.080 |
| Silver (Ag), % | 0 | |
| 0.027 to 0.1 |
| Zinc (Zn), % | 0 to 0.0020 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.2 |