C14181 Copper vs. C94900 Bronze
Both C14181 copper and C94900 bronze are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 80% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C14181 copper and the bottom bar is C94900 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Elongation at Break, % | 15 | |
| 17 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 43 | |
| 41 |
| Tensile Strength: Ultimate (UTS), MPa | 210 | |
| 300 |
| Tensile Strength: Yield (Proof), MPa | 130 | |
| 130 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 170 |
| Melting Completion (Liquidus), °C | 1080 | |
| 980 |
| Melting Onset (Solidus), °C | 1080 | |
| 910 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 370 |
| Thermal Expansion, µm/m-K | 17 | |
| 18 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 32 |
| Density, g/cm3 | 9.0 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 3.4 |
| Embodied Energy, MJ/kg | 41 | |
| 55 |
| Embodied Water, L/kg | 310 | |
| 350 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 28 | |
| 41 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 69 | |
| 72 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 6.9 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 6.5 | |
| 9.4 |
| Strength to Weight: Bending, points | 8.8 | |
| 11 |
| Thermal Shock Resistance, points | 7.4 | |
| 11 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 0 to 0.25 |
| Cadmium (Cd), % | 0 to 0.0020 | |
| 0 |
| Carbon (C), % | 0 to 0.0050 | |
| 0 |
| Copper (Cu), % | 99.9 to 100 | |
| 79 to 81 |
| Iron (Fe), % | 0 | |
| 0 to 0.3 |
| Lead (Pb), % | 0 to 0.0020 | |
| 4.0 to 6.0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 | |
| 4.0 to 6.0 |
| Phosphorus (P), % | 0 to 0.0020 | |
| 0 to 0.050 |
| Silicon (Si), % | 0 | |
| 0 to 0.0050 |
| Sulfur (S), % | 0 | |
| 0 to 0.080 |
| Tin (Sn), % | 0 | |
| 4.0 to 6.0 |
| Zinc (Zn), % | 0 to 0.0020 | |
| 4.0 to 6.0 |
| Residuals, % | 0 | |
| 0 to 0.8 |