C14200 Copper vs. SAE-AISI 1108 Steel
C14200 copper belongs to the copper alloys classification, while SAE-AISI 1108 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C14200 copper and the bottom bar is SAE-AISI 1108 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Elongation at Break, % | 8.0 to 45 | |
| 23 to 34 |
| Fatigue Strength, MPa | 76 to 130 | |
| 170 to 260 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 43 | |
| 73 |
| Shear Strength, MPa | 150 to 200 | |
| 250 to 280 |
| Tensile Strength: Ultimate (UTS), MPa | 220 to 370 | |
| 380 to 440 |
| Tensile Strength: Yield (Proof), MPa | 75 to 340 | |
| 220 to 360 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 400 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1460 |
| Melting Onset (Solidus), °C | 1030 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Conductivity, W/m-K | 190 | |
| 52 |
| Thermal Expansion, µm/m-K | 17 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 45 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 45 | |
| 8.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 1.8 |
| Density, g/cm3 | 8.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 1.4 |
| Embodied Energy, MJ/kg | 41 | |
| 18 |
| Embodied Water, L/kg | 310 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 29 to 83 | |
| 95 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 24 to 500 | |
| 130 to 340 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 24 |
| Strength to Weight: Axial, points | 6.8 to 11 | |
| 13 to 16 |
| Strength to Weight: Bending, points | 9.1 to 13 | |
| 15 to 16 |
| Thermal Diffusivity, mm2/s | 56 | |
| 14 |
| Thermal Shock Resistance, points | 7.9 to 13 | |
| 12 to 14 |
Alloy Composition
| Arsenic (As), % | 0.15 to 0.5 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.080 to 0.13 |
| Copper (Cu), % | 99.4 to 99.835 | |
| 0 |
| Iron (Fe), % | 0 | |
| 98.9 to 99.24 |
| Manganese (Mn), % | 0 | |
| 0.6 to 0.8 |
| Phosphorus (P), % | 0.015 to 0.040 | |
| 0 to 0.040 |
| Sulfur (S), % | 0 | |
| 0.080 to 0.13 |