C14300 Copper vs. AISI 403 Stainless Steel
C14300 copper belongs to the copper alloys classification, while AISI 403 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C14300 copper and the bottom bar is AISI 403 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Elongation at Break, % | 2.0 to 42 | |
| 16 to 25 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 43 | |
| 76 |
| Shear Strength, MPa | 150 to 260 | |
| 340 to 480 |
| Tensile Strength: Ultimate (UTS), MPa | 220 to 460 | |
| 530 to 780 |
| Tensile Strength: Yield (Proof), MPa | 76 to 430 | |
| 280 to 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 740 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1450 |
| Melting Onset (Solidus), °C | 1050 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 480 |
| Thermal Conductivity, W/m-K | 380 | |
| 28 |
| Thermal Expansion, µm/m-K | 17 | |
| 9.9 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 96 | |
| 2.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 96 | |
| 3.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 6.5 |
| Density, g/cm3 | 9.0 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 1.9 |
| Embodied Energy, MJ/kg | 41 | |
| 27 |
| Embodied Water, L/kg | 310 | |
| 99 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 9.0 to 72 | |
| 110 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 25 to 810 | |
| 210 to 840 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 14 |
| Stiffness to Weight: Bending, points | 18 | |
| 25 |
| Strength to Weight: Axial, points | 6.8 to 14 | |
| 19 to 28 |
| Strength to Weight: Bending, points | 9.1 to 15 | |
| 19 to 24 |
| Thermal Diffusivity, mm2/s | 110 | |
| 7.6 |
| Thermal Shock Resistance, points | 7.8 to 16 | |
| 20 to 29 |
Alloy Composition
| Cadmium (Cd), % | 0.050 to 0.15 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.15 |
| Chromium (Cr), % | 0 | |
| 11.5 to 13 |
| Copper (Cu), % | 99.9 to 99.95 | |
| 0 |
| Iron (Fe), % | 0 | |
| 84.7 to 88.5 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 | |
| 0 to 0.6 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |