C14300 Copper vs. C67600 Bronze
Both C14300 copper and C67600 bronze are copper alloys. They have 59% of their average alloy composition in common.
For each property being compared, the top bar is C14300 copper and the bottom bar is C67600 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 100 |
| Elongation at Break, % | 2.0 to 42 | |
| 13 to 33 |
| Poisson's Ratio | 0.34 | |
| 0.31 |
| Shear Modulus, GPa | 43 | |
| 40 |
| Shear Strength, MPa | 150 to 260 | |
| 270 to 350 |
| Tensile Strength: Ultimate (UTS), MPa | 220 to 460 | |
| 430 to 570 |
| Tensile Strength: Yield (Proof), MPa | 76 to 430 | |
| 170 to 380 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 120 |
| Melting Completion (Liquidus), °C | 1080 | |
| 890 |
| Melting Onset (Solidus), °C | 1050 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 380 |
| Thermal Conductivity, W/m-K | 380 | |
| 110 |
| Thermal Expansion, µm/m-K | 17 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 96 | |
| 24 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 96 | |
| 27 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 23 |
| Density, g/cm3 | 9.0 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 2.8 |
| Embodied Energy, MJ/kg | 41 | |
| 47 |
| Embodied Water, L/kg | 310 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 9.0 to 72 | |
| 63 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 25 to 810 | |
| 140 to 680 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 18 | |
| 20 |
| Strength to Weight: Axial, points | 6.8 to 14 | |
| 15 to 20 |
| Strength to Weight: Bending, points | 9.1 to 15 | |
| 16 to 19 |
| Thermal Diffusivity, mm2/s | 110 | |
| 35 |
| Thermal Shock Resistance, points | 7.8 to 16 | |
| 14 to 19 |
Alloy Composition
| Cadmium (Cd), % | 0.050 to 0.15 | |
| 0 |
| Copper (Cu), % | 99.9 to 99.95 | |
| 57 to 60 |
| Iron (Fe), % | 0 | |
| 0.4 to 1.3 |
| Lead (Pb), % | 0 | |
| 0.5 to 1.0 |
| Manganese (Mn), % | 0 | |
| 0.050 to 0.5 |
| Tin (Sn), % | 0 | |
| 0.5 to 1.5 |
| Zinc (Zn), % | 0 | |
| 35.2 to 41.6 |
| Residuals, % | 0 | |
| 0 to 0.5 |