C14300 Copper vs. N08700 Stainless Steel

C14300 copper belongs to the copper alloys classification, while N08700 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is C14300 copper and the bottom bar is N08700 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
200
Elongation at Break, % 2.0 to 42
32
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 43
79
Shear Strength, MPa 150 to 260
410
Tensile Strength: Ultimate (UTS), MPa 220 to 460
620
Tensile Strength: Yield (Proof), MPa 76 to 430
270

Thermal Properties

Latent Heat of Fusion, J/g 210
300
Maximum Temperature: Mechanical, °C 220
1100
Melting Completion (Liquidus), °C 1080
1450
Melting Onset (Solidus), °C 1050
1400
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 380
13
Thermal Expansion, µm/m-K 17
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 96
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 96
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 31
32
Density, g/cm3 9.0
8.1
Embodied Carbon, kg CO2/kg material 2.6
6.0
Embodied Energy, MJ/kg 41
82
Embodied Water, L/kg 310
200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 9.0 to 72
160
Resilience: Unit (Modulus of Resilience), kJ/m3 25 to 810
180
Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 18
24
Strength to Weight: Axial, points 6.8 to 14
21
Strength to Weight: Bending, points 9.1 to 15
20
Thermal Diffusivity, mm2/s 110
3.5
Thermal Shock Resistance, points 7.8 to 16
14

Alloy Composition

Cadmium (Cd), % 0.050 to 0.15
0
Carbon (C), % 0
0 to 0.040
Chromium (Cr), % 0
19 to 23
Copper (Cu), % 99.9 to 99.95
0 to 0.5
Iron (Fe), % 0
42 to 52.7
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 0
4.3 to 5.0
Nickel (Ni), % 0
24 to 26
Niobium (Nb), % 0
0 to 0.4
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.030