C14500 Copper vs. EN 1.5501 Steel

C14500 copper belongs to the copper alloys classification, while EN 1.5501 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is C14500 copper and the bottom bar is EN 1.5501 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
190
Elongation at Break, % 12 to 50
12 to 17
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 43
73
Shear Strength, MPa 150 to 190
270 to 310
Tensile Strength: Ultimate (UTS), MPa 220 to 330
390 to 510
Tensile Strength: Yield (Proof), MPa 69 to 260
260 to 420

Thermal Properties

Latent Heat of Fusion, J/g 210
250
Maximum Temperature: Mechanical, °C 200
400
Melting Completion (Liquidus), °C 1080
1460
Melting Onset (Solidus), °C 1050
1420
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 360
52
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 94
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 95
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 33
1.8
Density, g/cm3 8.9
7.9
Embodied Carbon, kg CO2/kg material 2.6
1.4
Embodied Energy, MJ/kg 42
18
Embodied Water, L/kg 310
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 36 to 85
40 to 83
Resilience: Unit (Modulus of Resilience), kJ/m3 21 to 300
190 to 460
Stiffness to Weight: Axial, points 7.2
13
Stiffness to Weight: Bending, points 18
24
Strength to Weight: Axial, points 6.8 to 10
14 to 18
Strength to Weight: Bending, points 9.1 to 12
15 to 18
Thermal Diffusivity, mm2/s 100
14
Thermal Shock Resistance, points 8.0 to 12
11 to 15

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0
0.13 to 0.16
Copper (Cu), % 99.2 to 99.596
0 to 0.25
Iron (Fe), % 0
98.4 to 99.269
Manganese (Mn), % 0
0.6 to 0.8
Phosphorus (P), % 0.0040 to 0.012
0 to 0.025
Silicon (Si), % 0
0 to 0.3
Sulfur (S), % 0
0 to 0.025
Tellurium (Te), % 0.4 to 0.7
0