C14510 Copper vs. 70Ag-30Ni Alloy
C14510 copper belongs to the copper alloys classification, while 70Ag-30Ni alloy belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is C14510 copper and the bottom bar is 70Ag-30Ni alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 100 |
| Poisson's Ratio | 0.34 | |
| 0.35 |
| Shear Modulus, GPa | 43 | |
| 39 |
| Tensile Strength: Ultimate (UTS), MPa | 300 to 320 | |
| 320 to 530 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 170 |
| Melting Completion (Liquidus), °C | 1080 | |
| 960 |
| Melting Onset (Solidus), °C | 1050 | |
| 960 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 300 |
| Thermal Expansion, µm/m-K | 17 | |
| 17 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.9 | |
| 10 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 5.8 |
| Stiffness to Weight: Bending, points | 18 | |
| 16 |
| Strength to Weight: Axial, points | 9.2 to 10 | |
| 8.8 to 15 |
| Strength to Weight: Bending, points | 11 to 12 | |
| 10 to 15 |
| Thermal Shock Resistance, points | 11 to 12 | |
| 13 to 21 |
Alloy Composition
| Copper (Cu), % | 99.15 to 99.69 | |
| 0 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 28.8 to 31 |
| Phosphorus (P), % | 0.010 to 0.030 | |
| 0 |
| Silver (Ag), % | 0 | |
| 69 to 71 |
| Tellurium (Te), % | 0.3 to 0.7 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.2 |