C14520 Copper vs. C83300 Brass
Both C14520 copper and C83300 brass are copper alloys. They have a moderately high 93% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C14520 copper and the bottom bar is C83300 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Elongation at Break, % | 9.0 to 9.6 | |
| 35 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 43 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 290 to 330 | |
| 220 |
| Tensile Strength: Yield (Proof), MPa | 230 to 250 | |
| 69 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 180 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1060 |
| Melting Onset (Solidus), °C | 1050 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 380 |
| Thermal Conductivity, W/m-K | 320 | |
| 160 |
| Thermal Expansion, µm/m-K | 17 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 85 | |
| 32 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 85 | |
| 33 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 30 |
| Density, g/cm3 | 8.9 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 2.7 |
| Embodied Energy, MJ/kg | 42 | |
| 44 |
| Embodied Water, L/kg | 310 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 24 to 29 | |
| 60 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 240 to 280 | |
| 21 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.0 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 9.0 to 10 | |
| 6.9 |
| Strength to Weight: Bending, points | 11 to 12 | |
| 9.2 |
| Thermal Diffusivity, mm2/s | 94 | |
| 48 |
| Thermal Shock Resistance, points | 10 to 12 | |
| 7.9 |
Alloy Composition
| Copper (Cu), % | 99.2 to 99.596 | |
| 92 to 94 |
| Lead (Pb), % | 0 | |
| 1.0 to 2.0 |
| Phosphorus (P), % | 0.0040 to 0.020 | |
| 0 |
| Tellurium (Te), % | 0.4 to 0.7 | |
| 0 |
| Tin (Sn), % | 0 | |
| 1.0 to 2.0 |
| Zinc (Zn), % | 0 | |
| 2.0 to 6.0 |
| Residuals, % | 0 | |
| 0 to 0.7 |