C14520 Copper vs. S28200 Stainless Steel
C14520 copper belongs to the copper alloys classification, while S28200 stainless steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is C14520 copper and the bottom bar is S28200 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 200 |
| Elongation at Break, % | 9.0 to 9.6 | |
| 45 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 43 | |
| 77 |
| Shear Strength, MPa | 170 to 190 | |
| 610 |
| Tensile Strength: Ultimate (UTS), MPa | 290 to 330 | |
| 870 |
| Tensile Strength: Yield (Proof), MPa | 230 to 250 | |
| 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 900 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1380 |
| Melting Onset (Solidus), °C | 1050 | |
| 1330 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 480 |
| Thermal Expansion, µm/m-K | 17 | |
| 18 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 12 |
| Density, g/cm3 | 8.9 | |
| 7.6 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 2.8 |
| Embodied Energy, MJ/kg | 42 | |
| 41 |
| Embodied Water, L/kg | 310 | |
| 160 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 24 to 29 | |
| 330 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 240 to 280 | |
| 540 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 15 |
| Stiffness to Weight: Bending, points | 18 | |
| 26 |
| Strength to Weight: Axial, points | 9.0 to 10 | |
| 32 |
| Strength to Weight: Bending, points | 11 to 12 | |
| 27 |
| Thermal Shock Resistance, points | 10 to 12 | |
| 17 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.15 |
| Chromium (Cr), % | 0 | |
| 17 to 19 |
| Copper (Cu), % | 99.2 to 99.596 | |
| 0.75 to 1.3 |
| Iron (Fe), % | 0 | |
| 57.7 to 64.1 |
| Manganese (Mn), % | 0 | |
| 17 to 19 |
| Molybdenum (Mo), % | 0 | |
| 0.75 to 1.3 |
| Nitrogen (N), % | 0 | |
| 0.4 to 0.6 |
| Phosphorus (P), % | 0.0040 to 0.020 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tellurium (Te), % | 0.4 to 0.7 | |
| 0 |