C15000 Copper vs. C46200 Brass
Both C15000 copper and C46200 brass are copper alloys. They have 64% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C15000 copper and the bottom bar is C46200 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 100 |
| Elongation at Break, % | 13 to 54 | |
| 17 to 34 |
| Poisson's Ratio | 0.34 | |
| 0.31 |
| Shear Modulus, GPa | 43 | |
| 40 |
| Shear Strength, MPa | 150 to 280 | |
| 240 to 290 |
| Tensile Strength: Ultimate (UTS), MPa | 200 to 460 | |
| 370 to 480 |
| Tensile Strength: Yield (Proof), MPa | 45 to 460 | |
| 120 to 290 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 120 |
| Melting Completion (Liquidus), °C | 1080 | |
| 840 |
| Melting Onset (Solidus), °C | 980 | |
| 800 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 380 |
| Thermal Conductivity, W/m-K | 370 | |
| 110 |
| Thermal Expansion, µm/m-K | 17 | |
| 20 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 24 |
| Density, g/cm3 | 9.0 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.7 |
| Embodied Energy, MJ/kg | 43 | |
| 46 |
| Embodied Water, L/kg | 310 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 19 to 250 | |
| 69 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 8.7 to 910 | |
| 72 to 400 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 6.2 to 14 | |
| 13 to 16 |
| Strength to Weight: Bending, points | 8.5 to 15 | |
| 14 to 17 |
| Thermal Diffusivity, mm2/s | 110 | |
| 35 |
| Thermal Shock Resistance, points | 7.3 to 17 | |
| 12 to 16 |
Alloy Composition
| Copper (Cu), % | 99.8 to 99.9 | |
| 62 to 65 |
| Iron (Fe), % | 0 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 0 to 0.2 |
| Tin (Sn), % | 0 | |
| 0.5 to 1.0 |
| Zinc (Zn), % | 0 | |
| 33.3 to 37.5 |
| Zirconium (Zr), % | 0.1 to 0.2 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |