C15500 Copper vs. C67400 Bronze
Both C15500 copper and C67400 bronze are copper alloys. They have 59% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C15500 copper and the bottom bar is C67400 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Elongation at Break, % | 3.0 to 37 | |
| 22 to 28 |
| Poisson's Ratio | 0.34 | |
| 0.31 |
| Shear Modulus, GPa | 43 | |
| 41 |
| Shear Strength, MPa | 190 to 320 | |
| 310 to 350 |
| Tensile Strength: Ultimate (UTS), MPa | 280 to 550 | |
| 480 to 610 |
| Tensile Strength: Yield (Proof), MPa | 130 to 530 | |
| 250 to 370 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 130 |
| Melting Completion (Liquidus), °C | 1080 | |
| 890 |
| Melting Onset (Solidus), °C | 1080 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 400 |
| Thermal Conductivity, W/m-K | 350 | |
| 100 |
| Thermal Expansion, µm/m-K | 17 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 90 | |
| 23 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 91 | |
| 26 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 33 | |
| 23 |
| Density, g/cm3 | 8.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.8 |
| Embodied Energy, MJ/kg | 42 | |
| 48 |
| Embodied Water, L/kg | 360 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 15 to 84 | |
| 110 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 72 to 1210 | |
| 300 to 660 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 18 | |
| 20 |
| Strength to Weight: Axial, points | 8.6 to 17 | |
| 17 to 22 |
| Strength to Weight: Bending, points | 11 to 17 | |
| 17 to 20 |
| Thermal Diffusivity, mm2/s | 100 | |
| 32 |
| Thermal Shock Resistance, points | 9.8 to 20 | |
| 16 to 20 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.5 to 2.0 |
| Copper (Cu), % | 99.75 to 99.853 | |
| 57 to 60 |
| Iron (Fe), % | 0 | |
| 0 to 0.35 |
| Lead (Pb), % | 0 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 0.080 to 0.13 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 2.0 to 3.5 |
| Nickel (Ni), % | 0 | |
| 0 to 0.25 |
| Phosphorus (P), % | 0.040 to 0.080 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0.5 to 1.5 |
| Silver (Ag), % | 0.027 to 0.1 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.3 |
| Zinc (Zn), % | 0 | |
| 31.1 to 40 |
| Residuals, % | 0 | |
| 0 to 0.5 |