C15900 Copper vs. R05252 Alloy

C15900 copper belongs to the copper alloys classification, while R05252 alloy belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is C15900 copper and the bottom bar is R05252 alloy.

UNS C15900 Dispersion Strengthened Copper UNS R05252 Tantalum-Tungsten Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		110
Elastic (Young's, Tensile) Modulus, GPa		200

Elongation at Break, %		6.5
Elongation at Break, %		23

Poisson's Ratio		0.34
Poisson's Ratio		0.33

Shear Modulus, GPa		43
Shear Modulus, GPa		73

Tensile Strength: Ultimate (UTS), MPa		720
Tensile Strength: Ultimate (UTS), MPa		310

Tensile Strength: Yield (Proof), MPa		240
Tensile Strength: Yield (Proof), MPa		220

Thermal Properties

Latent Heat of Fusion, J/g		210
Latent Heat of Fusion, J/g		140

Specific Heat Capacity, J/kg-K		390
Specific Heat Capacity, J/kg-K		140

Thermal Expansion, µm/m-K		17
Thermal Expansion, µm/m-K		6.7

Otherwise Unclassified Properties

Density, g/cm³		8.8
Density, g/cm³		17

Embodied Water, L/kg		310
Embodied Water, L/kg		600

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m³		37
Resilience: Ultimate (Unit Rupture Work), MJ/m³		63

Resilience: Unit (Modulus of Resilience), kJ/m³		260
Resilience: Unit (Modulus of Resilience), kJ/m³		120

Stiffness to Weight: Axial, points		7.2
Stiffness to Weight: Axial, points		6.5

Stiffness to Weight: Bending, points		18
Stiffness to Weight: Bending, points		12

Strength to Weight: Axial, points		23
Strength to Weight: Axial, points		5.2

Strength to Weight: Bending, points		20
Strength to Weight: Bending, points		6.1

Thermal Shock Resistance, points		26
Thermal Shock Resistance, points		17

Alloy Composition

Aluminum (Al), %		0.76 to 0.84
Aluminum (Al), %		0

Carbon (C), %		0.27 to 0.33
Carbon (C), %		0 to 0.010

Copper (Cu), %		97.5 to 97.9
Copper (Cu), %		0

Hydrogen (H), %		0
Hydrogen (H), %		0 to 0.0015

Iron (Fe), %		0 to 0.040
Iron (Fe), %		0 to 0.010

Molybdenum (Mo), %		0
Molybdenum (Mo), %		0 to 0.020

Nickel (Ni), %		0
Nickel (Ni), %		0 to 0.010

Niobium (Nb), %		0
Niobium (Nb), %		0 to 0.1

Nitrogen (N), %		0
Nitrogen (N), %		0 to 0.010

Oxygen (O), %		0.4 to 0.54
Oxygen (O), %		0 to 0.015

Silicon (Si), %		0
Silicon (Si), %		0 to 0.0050

Tantalum (Ta), %		0
Tantalum (Ta), %		88.8 to 91

Titanium (Ti), %		0.66 to 0.74
Titanium (Ti), %		0 to 0.010

Tungsten (W), %		0
Tungsten (W), %		9.0 to 11