C17000 Copper vs. 358.0 Aluminum
C17000 copper belongs to the copper alloys classification, while 358.0 aluminum belongs to the aluminum alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is C17000 copper and the bottom bar is 358.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 71 |
| Elongation at Break, % | 1.1 to 31 | |
| 3.5 to 6.0 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 45 | |
| 27 |
| Shear Strength, MPa | 320 to 750 | |
| 300 to 320 |
| Tensile Strength: Ultimate (UTS), MPa | 490 to 1310 | |
| 350 to 370 |
| Tensile Strength: Yield (Proof), MPa | 160 to 1140 | |
| 290 to 320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 520 |
| Maximum Temperature: Mechanical, °C | 270 | |
| 170 |
| Melting Completion (Liquidus), °C | 980 | |
| 600 |
| Melting Onset (Solidus), °C | 870 | |
| 560 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 900 |
| Thermal Conductivity, W/m-K | 110 | |
| 150 |
| Thermal Expansion, µm/m-K | 17 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 22 | |
| 36 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 22 | |
| 130 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.8 | |
| 2.6 |
| Embodied Carbon, kg CO2/kg material | 8.7 | |
| 8.7 |
| Embodied Energy, MJ/kg | 140 | |
| 160 |
| Embodied Water, L/kg | 310 | |
| 1090 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.2 to 390 | |
| 12 to 20 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 to 5420 | |
| 590 to 710 |
| Stiffness to Weight: Axial, points | 7.6 | |
| 15 |
| Stiffness to Weight: Bending, points | 19 | |
| 53 |
| Strength to Weight: Axial, points | 15 to 41 | |
| 37 to 39 |
| Strength to Weight: Bending, points | 16 to 30 | |
| 42 to 44 |
| Thermal Diffusivity, mm2/s | 32 | |
| 63 |
| Thermal Shock Resistance, points | 17 to 45 | |
| 16 to 17 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.2 | |
| 89.1 to 91.8 |
| Beryllium (Be), % | 1.6 to 1.8 | |
| 0.1 to 0.3 |
| Chromium (Cr), % | 0 | |
| 0 to 0.2 |
| Copper (Cu), % | 96.3 to 98.2 | |
| 0 to 0.2 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 to 0.3 |
| Magnesium (Mg), % | 0 | |
| 0.4 to 0.6 |
| Manganese (Mn), % | 0 | |
| 0 to 0.2 |
| Nickel (Ni), % | 0.2 to 0.6 | |
| 0 |
| Silicon (Si), % | 0 to 0.2 | |
| 7.6 to 8.6 |
| Titanium (Ti), % | 0 | |
| 0.1 to 0.2 |
| Zinc (Zn), % | 0 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.15 |