C17000 Copper vs. 88-silver 12-tin-oxide
C17000 copper belongs to the copper alloys classification, while 88-silver 12-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (23, in this case) are not shown.
For each property being compared, the top bar is C17000 copper and the bottom bar is 88-silver 12-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 22 | |
| 84 to 86 |
| Elongation at Break, % | 1.1 to 31 | |
| 9.0 to 37 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.2 to 390 | |
| 24 to 70 |
| Shear Strength, MPa | 320 to 750 | |
| 150 to 160 |
| Tensile Strength: Ultimate (UTS), MPa | 490 to 1310 | |
| 230 to 280 |
| Tensile Strength: Yield (Proof), MPa | 160 to 1140 | |
| 110 to 260 |