C17000 Copper vs. Nickel 718
C17000 copper belongs to the copper alloys classification, while nickel 718 belongs to the nickel alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C17000 copper and the bottom bar is nickel 718.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Elongation at Break, % | 1.1 to 31 | |
| 12 to 50 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Rockwell C Hardness | 21 to 42 | |
| 40 |
| Shear Modulus, GPa | 45 | |
| 75 |
| Shear Strength, MPa | 320 to 750 | |
| 660 to 950 |
| Tensile Strength: Ultimate (UTS), MPa | 490 to 1310 | |
| 930 to 1530 |
| Tensile Strength: Yield (Proof), MPa | 160 to 1140 | |
| 510 to 1330 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 310 |
| Maximum Temperature: Mechanical, °C | 270 | |
| 980 |
| Melting Completion (Liquidus), °C | 980 | |
| 1340 |
| Melting Onset (Solidus), °C | 870 | |
| 1260 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 450 |
| Thermal Conductivity, W/m-K | 110 | |
| 11 |
| Thermal Expansion, µm/m-K | 17 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 22 | |
| 1.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 22 | |
| 1.5 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.8 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 8.7 | |
| 13 |
| Embodied Energy, MJ/kg | 140 | |
| 190 |
| Embodied Water, L/kg | 310 | |
| 250 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.2 to 390 | |
| 140 to 390 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 to 5420 | |
| 660 to 4560 |
| Stiffness to Weight: Axial, points | 7.6 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 23 |
| Strength to Weight: Axial, points | 15 to 41 | |
| 31 to 51 |
| Strength to Weight: Bending, points | 16 to 30 | |
| 25 to 35 |
| Thermal Diffusivity, mm2/s | 32 | |
| 3.0 |
| Thermal Shock Resistance, points | 17 to 45 | |
| 27 to 44 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.2 | |
| 0.2 to 0.8 |
| Beryllium (Be), % | 1.6 to 1.8 | |
| 0 |
| Boron (B), % | 0 | |
| 0 to 0.0060 |
| Carbon (C), % | 0 | |
| 0 to 0.080 |
| Chromium (Cr), % | 0 | |
| 17 to 21 |
| Cobalt (Co), % | 0 | |
| 0 to 1.0 |
| Copper (Cu), % | 96.3 to 98.2 | |
| 0 to 0.3 |
| Iron (Fe), % | 0 to 0.4 | |
| 11.1 to 24.6 |
| Manganese (Mn), % | 0 | |
| 0 to 0.35 |
| Molybdenum (Mo), % | 0 | |
| 2.8 to 3.3 |
| Nickel (Ni), % | 0.2 to 0.6 | |
| 50 to 55 |
| Niobium (Nb), % | 0 | |
| 4.8 to 5.5 |
| Phosphorus (P), % | 0 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 to 0.35 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 0.65 to 1.2 |
| Residuals, % | 0 to 0.5 | |
| 0 |