C17200 Copper vs. S43932 Stainless Steel

C17200 copper belongs to the copper alloys classification, while S43932 stainless steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is C17200 copper and the bottom bar is S43932 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
200
Elongation at Break, % 1.1 to 37
25
Poisson's Ratio 0.33
0.28
Shear Modulus, GPa 45
77
Shear Strength, MPa 330 to 780
300
Tensile Strength: Ultimate (UTS), MPa 480 to 1380
460
Tensile Strength: Yield (Proof), MPa 160 to 1250
230

Thermal Properties

Latent Heat of Fusion, J/g 230
280
Maximum Temperature: Mechanical, °C 280
890
Melting Completion (Liquidus), °C 980
1440
Melting Onset (Solidus), °C 870
1400
Specific Heat Capacity, J/kg-K 390
480
Thermal Conductivity, W/m-K 110
23
Thermal Expansion, µm/m-K 18
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 22
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 23
3.2

Otherwise Unclassified Properties

Density, g/cm3 8.8
7.7
Embodied Carbon, kg CO2/kg material 9.4
2.7
Embodied Energy, MJ/kg 150
40
Embodied Water, L/kg 310
120

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 4.2 to 500
96
Resilience: Unit (Modulus of Resilience), kJ/m3 110 to 5720
140
Stiffness to Weight: Axial, points 7.6
14
Stiffness to Weight: Bending, points 19
25
Strength to Weight: Axial, points 15 to 44
17
Strength to Weight: Bending, points 16 to 31
17
Thermal Diffusivity, mm2/s 31
6.3
Thermal Shock Resistance, points 16 to 46
16

Alloy Composition

Aluminum (Al), % 0 to 0.2
0 to 0.15
Beryllium (Be), % 1.8 to 2.0
0
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
17 to 19
Copper (Cu), % 96.1 to 98
0
Iron (Fe), % 0 to 0.4
76.7 to 83
Manganese (Mn), % 0
0 to 1.0
Nickel (Ni), % 0.2 to 0.6
0 to 0.5
Niobium (Nb), % 0
0.2 to 0.75
Nitrogen (N), % 0
0 to 0.030
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.2
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Titanium (Ti), % 0
0.2 to 0.75
Residuals, % 0 to 0.5
0