C17300 Copper vs. N06230 Nickel
C17300 copper belongs to the copper alloys classification, while N06230 nickel belongs to the nickel alloys. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C17300 copper and the bottom bar is N06230 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 210 |
| Elongation at Break, % | 3.0 to 23 | |
| 38 to 48 |
| Poisson's Ratio | 0.33 | |
| 0.28 |
| Shear Modulus, GPa | 45 | |
| 83 |
| Shear Strength, MPa | 320 to 790 | |
| 420 to 600 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 1380 | |
| 620 to 840 |
| Tensile Strength: Yield (Proof), MPa | 160 to 1200 | |
| 330 to 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 310 |
| Maximum Temperature: Mechanical, °C | 270 | |
| 990 |
| Melting Completion (Liquidus), °C | 980 | |
| 1370 |
| Melting Onset (Solidus), °C | 870 | |
| 1300 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 420 |
| Thermal Conductivity, W/m-K | 110 | |
| 8.9 |
| Thermal Expansion, µm/m-K | 17 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 22 | |
| 1.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 23 | |
| 1.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.8 | |
| 9.5 |
| Embodied Carbon, kg CO2/kg material | 9.4 | |
| 11 |
| Embodied Energy, MJ/kg | 150 | |
| 160 |
| Embodied Water, L/kg | 310 | |
| 290 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 40 to 88 | |
| 200 to 330 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 to 5410 | |
| 250 to 380 |
| Stiffness to Weight: Axial, points | 7.6 | |
| 12 |
| Stiffness to Weight: Bending, points | 19 | |
| 21 |
| Strength to Weight: Axial, points | 16 to 44 | |
| 18 to 25 |
| Strength to Weight: Bending, points | 16 to 31 | |
| 17 to 21 |
| Thermal Diffusivity, mm2/s | 32 | |
| 2.3 |
| Thermal Shock Resistance, points | 17 to 48 | |
| 17 to 23 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.2 | |
| 0.2 to 0.5 |
| Beryllium (Be), % | 1.8 to 2.0 | |
| 0 |
| Boron (B), % | 0 | |
| 0 to 0.015 |
| Carbon (C), % | 0 | |
| 0.050 to 0.15 |
| Chromium (Cr), % | 0 | |
| 20 to 24 |
| Cobalt (Co), % | 0 | |
| 0 to 5.0 |
| Copper (Cu), % | 95.5 to 97.8 | |
| 0 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 to 3.0 |
| Lanthanum (La), % | 0 | |
| 0.0050 to 0.050 |
| Lead (Pb), % | 0.2 to 0.6 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.3 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 1.0 to 3.0 |
| Nickel (Ni), % | 0.2 to 0.6 | |
| 47.5 to 65.2 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.2 | |
| 0.25 to 0.75 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Tungsten (W), % | 0 | |
| 13 to 15 |
| Residuals, % | 0 to 0.5 | |
| 0 |