C17500 Copper vs. EN 1.4415 Stainless Steel
C17500 copper belongs to the copper alloys classification, while EN 1.4415 stainless steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C17500 copper and the bottom bar is EN 1.4415 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 200 |
| Elongation at Break, % | 6.0 to 30 | |
| 17 to 20 |
| Fatigue Strength, MPa | 170 to 310 | |
| 470 to 510 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 45 | |
| 77 |
| Shear Strength, MPa | 200 to 520 | |
| 520 to 570 |
| Tensile Strength: Ultimate (UTS), MPa | 310 to 860 | |
| 830 to 930 |
| Tensile Strength: Yield (Proof), MPa | 170 to 760 | |
| 730 to 840 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 790 |
| Melting Completion (Liquidus), °C | 1060 | |
| 1460 |
| Melting Onset (Solidus), °C | 1020 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Conductivity, W/m-K | 200 | |
| 19 |
| Thermal Expansion, µm/m-K | 18 | |
| 9.9 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 24 to 53 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 24 to 54 | |
| 2.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 60 | |
| 13 |
| Density, g/cm3 | 8.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 4.7 | |
| 3.6 |
| Embodied Energy, MJ/kg | 73 | |
| 51 |
| Embodied Water, L/kg | 320 | |
| 120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 30 to 120 | |
| 150 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 to 2390 | |
| 1350 to 1790 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 14 |
| Stiffness to Weight: Bending, points | 18 | |
| 25 |
| Strength to Weight: Axial, points | 9.7 to 27 | |
| 29 to 33 |
| Strength to Weight: Bending, points | 11 to 23 | |
| 25 to 27 |
| Thermal Diffusivity, mm2/s | 59 | |
| 5.1 |
| Thermal Shock Resistance, points | 11 to 29 | |
| 30 to 34 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.2 | |
| 0 |
| Beryllium (Be), % | 0.4 to 0.7 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 | |
| 11.5 to 13.5 |
| Cobalt (Co), % | 2.4 to 2.7 | |
| 0 |
| Copper (Cu), % | 95.6 to 97.2 | |
| 0 |
| Iron (Fe), % | 0 to 0.1 | |
| 75.9 to 82.4 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0 | |
| 1.5 to 2.5 |
| Nickel (Ni), % | 0 | |
| 4.5 to 6.5 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 0 to 0.010 |
| Vanadium (V), % | 0 | |
| 0.1 to 0.5 |
| Residuals, % | 0 to 0.5 | |
| 0 |