C18100 Copper vs. C61500 Bronze
Both C18100 copper and C61500 bronze are copper alloys. They have a moderately high 90% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C18100 copper and the bottom bar is C61500 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Elongation at Break, % | 8.3 | |
| 3.0 to 55 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 47 | |
| 42 |
| Shear Strength, MPa | 300 | |
| 350 to 550 |
| Tensile Strength: Ultimate (UTS), MPa | 510 | |
| 480 to 970 |
| Tensile Strength: Yield (Proof), MPa | 460 | |
| 150 to 720 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 220 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 220 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1040 |
| Melting Onset (Solidus), °C | 1020 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 430 |
| Thermal Conductivity, W/m-K | 320 | |
| 58 |
| Thermal Expansion, µm/m-K | 17 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 80 | |
| 13 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 81 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 29 |
| Density, g/cm3 | 8.9 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 3.2 |
| Embodied Energy, MJ/kg | 43 | |
| 52 |
| Embodied Water, L/kg | 310 | |
| 380 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 40 | |
| 27 to 200 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 900 | |
| 100 to 2310 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 16 | |
| 16 to 32 |
| Strength to Weight: Bending, points | 16 | |
| 16 to 26 |
| Thermal Diffusivity, mm2/s | 94 | |
| 16 |
| Thermal Shock Resistance, points | 18 | |
| 17 to 34 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 7.7 to 8.3 |
| Chromium (Cr), % | 0.4 to 1.2 | |
| 0 |
| Copper (Cu), % | 98.7 to 99.49 | |
| 89 to 90.5 |
| Lead (Pb), % | 0 | |
| 0 to 0.015 |
| Magnesium (Mg), % | 0.030 to 0.060 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 1.8 to 2.2 |
| Zirconium (Zr), % | 0.080 to 0.2 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |