C18600 Copper vs. Type 3 Niobium
C18600 copper belongs to the copper alloys classification, while Type 3 niobium belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is C18600 copper and the bottom bar is Type 3 niobium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 100 |
| Elongation at Break, % | 8.0 to 11 | |
| 23 |
| Poisson's Ratio | 0.34 | |
| 0.4 |
| Shear Modulus, GPa | 44 | |
| 38 |
| Tensile Strength: Ultimate (UTS), MPa | 520 to 580 | |
| 220 |
| Tensile Strength: Yield (Proof), MPa | 500 to 520 | |
| 140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 310 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 270 |
| Thermal Conductivity, W/m-K | 280 | |
| 42 |
| Thermal Expansion, µm/m-K | 17 | |
| 7.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.9 | |
| 8.6 |
| Embodied Water, L/kg | 310 | |
| 160 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 44 to 58 | |
| 44 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1060 to 1180 | |
| 93 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 6.8 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 16 to 18 | |
| 7.2 |
| Strength to Weight: Bending, points | 16 to 17 | |
| 9.5 |
| Thermal Diffusivity, mm2/s | 81 | |
| 18 |
| Thermal Shock Resistance, points | 19 to 20 | |
| 21 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.010 |
| Chromium (Cr), % | 0.1 to 1.0 | |
| 0 |
| Cobalt (Co), % | 0 to 0.1 | |
| 0 |
| Copper (Cu), % | 96.5 to 99.55 | |
| 0 |
| Hafnium (Hf), % | 0 | |
| 0 to 0.020 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0015 |
| Iron (Fe), % | 0.25 to 0.8 | |
| 0 to 0.0050 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.010 |
| Nickel (Ni), % | 0 to 0.25 | |
| 0 to 0.0050 |
| Niobium (Nb), % | 0 | |
| 98.6 to 99.2 |
| Nitrogen (N), % | 0 | |
| 0 to 0.010 |
| Oxygen (O), % | 0 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 | |
| 0 to 0.0050 |
| Tantalum (Ta), % | 0 | |
| 0 to 0.1 |
| Titanium (Ti), % | 0.050 to 0.5 | |
| 0 to 0.020 |
| Tungsten (W), % | 0 | |
| 0 to 0.030 |
| Zirconium (Zr), % | 0.050 to 0.4 | |
| 0.8 to 1.2 |
| Residuals, % | 0 to 0.5 | |
| 0 |