C18600 Copper vs. N06250 Nickel
C18600 copper belongs to the copper alloys classification, while N06250 nickel belongs to the nickel alloys. There are 25 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C18600 copper and the bottom bar is N06250 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 210 |
| Elongation at Break, % | 8.0 to 11 | |
| 46 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 44 | |
| 82 |
| Shear Strength, MPa | 310 to 340 | |
| 500 |
| Tensile Strength: Ultimate (UTS), MPa | 520 to 580 | |
| 710 |
| Tensile Strength: Yield (Proof), MPa | 500 to 520 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 980 |
| Melting Completion (Liquidus), °C | 1090 | |
| 1490 |
| Melting Onset (Solidus), °C | 1070 | |
| 1440 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 440 |
| Thermal Expansion, µm/m-K | 17 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 55 |
| Density, g/cm3 | 8.9 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 10 |
| Embodied Energy, MJ/kg | 46 | |
| 140 |
| Embodied Water, L/kg | 310 | |
| 270 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 44 to 58 | |
| 260 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1060 to 1180 | |
| 170 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 14 |
| Stiffness to Weight: Bending, points | 18 | |
| 23 |
| Strength to Weight: Axial, points | 16 to 18 | |
| 23 |
| Strength to Weight: Bending, points | 16 to 17 | |
| 21 |
| Thermal Shock Resistance, points | 19 to 20 | |
| 19 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.020 |
| Chromium (Cr), % | 0.1 to 1.0 | |
| 20 to 23 |
| Cobalt (Co), % | 0 to 0.1 | |
| 0 |
| Copper (Cu), % | 96.5 to 99.55 | |
| 0.25 to 1.3 |
| Iron (Fe), % | 0.25 to 0.8 | |
| 7.4 to 19.4 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 10.1 to 12 |
| Nickel (Ni), % | 0 to 0.25 | |
| 50 to 54 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0 to 0.090 |
| Sulfur (S), % | 0 | |
| 0 to 0.0050 |
| Titanium (Ti), % | 0.050 to 0.5 | |
| 0 |
| Tungsten (W), % | 0 | |
| 0.25 to 1.3 |
| Zirconium (Zr), % | 0.050 to 0.4 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |