C19010 Copper vs. ASTM B685 Alloy

C19010 copper belongs to the copper alloys classification, while ASTM B685 alloy belongs to the otherwise unclassified metals. They have 40% of their average alloy composition in common. There are 17 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is C19010 copper and the bottom bar is ASTM B685 alloy.

UNS C19010 (CW109C) Nickel-Silicon Copper ASTM B685 Palladium-Copper Electrical Contact Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		120
Elastic (Young's, Tensile) Modulus, GPa		120

Poisson's Ratio		0.34
Poisson's Ratio		0.37

Shear Modulus, GPa		43
Shear Modulus, GPa		43

Tensile Strength: Ultimate (UTS), MPa		330 to 640
Tensile Strength: Ultimate (UTS), MPa		660 to 1060

Thermal Properties

Latent Heat of Fusion, J/g		210
Latent Heat of Fusion, J/g		180

Melting Completion (Liquidus), °C		1060
Melting Completion (Liquidus), °C		1230

Melting Onset (Solidus), °C		1010
Melting Onset (Solidus), °C		1200

Specific Heat Capacity, J/kg-K		390
Specific Heat Capacity, J/kg-K		300

Thermal Expansion, µm/m-K		17
Thermal Expansion, µm/m-K		14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS		48 to 63
Electrical Conductivity: Equal Volume, % IACS		5.0

Electrical Conductivity: Equal Weight (Specific), % IACS		48 to 63
Electrical Conductivity: Equal Weight (Specific), % IACS		4.1

Otherwise Unclassified Properties

Density, g/cm³		8.9
Density, g/cm³		11

Common Calculations

Stiffness to Weight: Axial, points		7.3
Stiffness to Weight: Axial, points		6.1

Stiffness to Weight: Bending, points		18
Stiffness to Weight: Bending, points		15

Strength to Weight: Axial, points		10 to 20
Strength to Weight: Axial, points		17 to 27

Strength to Weight: Bending, points		12 to 18
Strength to Weight: Bending, points		16 to 21

Thermal Shock Resistance, points		12 to 23
Thermal Shock Resistance, points		28 to 46

Alloy Composition

Aluminum (Al), %		0
Aluminum (Al), %		0 to 0.0050

Cadmium (Cd), %		0
Cadmium (Cd), %		0 to 0.050

Copper (Cu), %		97.3 to 99.04
Copper (Cu), %		39.5 to 40.5

Iron (Fe), %		0
Iron (Fe), %		0 to 0.050

Lead (Pb), %		0
Lead (Pb), %		0 to 0.030

Nickel (Ni), %		0.8 to 1.8
Nickel (Ni), %		0

Palladium (Pd), %		0
Palladium (Pd), %		59 to 60.5

Phosphorus (P), %		0.010 to 0.050
Phosphorus (P), %		0

Silicon (Si), %		0.15 to 0.35
Silicon (Si), %		0

Silver (Ag), %		0
Silver (Ag), %		0 to 0.1

Zinc (Zn), %		0
Zinc (Zn), %		0 to 0.060

Residuals, %		0
Residuals, %		0 to 0.2