C19010 Copper vs. C54400 Bronze
Both C19010 copper and C54400 bronze are copper alloys. They have 89% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is C19010 copper and the bottom bar is C54400 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 43 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 640 | |
| 330 to 720 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 170 |
| Melting Completion (Liquidus), °C | 1060 | |
| 1000 |
| Melting Onset (Solidus), °C | 1010 | |
| 930 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 370 |
| Thermal Conductivity, W/m-K | 260 | |
| 86 |
| Thermal Expansion, µm/m-K | 17 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 48 to 63 | |
| 19 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 48 to 63 | |
| 19 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 31 |
| Density, g/cm3 | 8.9 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.9 |
| Embodied Energy, MJ/kg | 42 | |
| 48 |
| Embodied Water, L/kg | 310 | |
| 340 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.3 | |
| 6.8 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 10 to 20 | |
| 10 to 22 |
| Strength to Weight: Bending, points | 12 to 18 | |
| 12 to 20 |
| Thermal Diffusivity, mm2/s | 75 | |
| 26 |
| Thermal Shock Resistance, points | 12 to 23 | |
| 12 to 26 |
Alloy Composition
| Copper (Cu), % | 97.3 to 99.04 | |
| 85.4 to 91.5 |
| Iron (Fe), % | 0 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 3.5 to 4.5 |
| Nickel (Ni), % | 0.8 to 1.8 | |
| 0 |
| Phosphorus (P), % | 0.010 to 0.050 | |
| 0.010 to 0.5 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0 |
| Tin (Sn), % | 0 | |
| 3.5 to 4.5 |
| Zinc (Zn), % | 0 | |
| 1.5 to 4.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |