C19025 Copper vs. EN 1.1233 Steel
C19025 copper belongs to the copper alloys classification, while EN 1.1233 steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C19025 copper and the bottom bar is EN 1.1233 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 43 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 620 | |
| 680 to 760 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 400 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1450 |
| Melting Onset (Solidus), °C | 1020 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 470 |
| Thermal Conductivity, W/m-K | 160 | |
| 51 |
| Thermal Expansion, µm/m-K | 17 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 40 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 40 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 1.9 |
| Density, g/cm3 | 8.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 1.4 |
| Embodied Energy, MJ/kg | 44 | |
| 19 |
| Embodied Water, L/kg | 320 | |
| 47 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 24 |
| Strength to Weight: Axial, points | 15 to 19 | |
| 24 to 27 |
| Strength to Weight: Bending, points | 15 to 18 | |
| 22 to 24 |
| Thermal Diffusivity, mm2/s | 47 | |
| 14 |
| Thermal Shock Resistance, points | 17 to 22 | |
| 22 to 24 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.050 |
| Carbon (C), % | 0 | |
| 0.52 to 0.6 |
| Copper (Cu), % | 97.1 to 98.5 | |
| 0 to 0.3 |
| Iron (Fe), % | 0 | |
| 98 to 99.1 |
| Manganese (Mn), % | 0 | |
| 0.9 to 1.2 |
| Nickel (Ni), % | 0.8 to 1.2 | |
| 0 |
| Oxygen (O), % | 0 | |
| 0 to 0.0020 |
| Phosphorus (P), % | 0.030 to 0.070 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 0.7 to 1.1 | |
| 0 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 |