C19200 Copper vs. EN 1.4310 Stainless Steel
C19200 copper belongs to the copper alloys classification, while EN 1.4310 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C19200 copper and the bottom bar is EN 1.4310 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 200 |
| Elongation at Break, % | 2.0 to 35 | |
| 14 to 45 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 44 | |
| 77 |
| Shear Strength, MPa | 190 to 300 | |
| 510 to 550 |
| Tensile Strength: Ultimate (UTS), MPa | 280 to 530 | |
| 730 to 900 |
| Tensile Strength: Yield (Proof), MPa | 98 to 510 | |
| 260 to 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 910 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1420 |
| Melting Onset (Solidus), °C | 1080 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 480 |
| Thermal Conductivity, W/m-K | 240 | |
| 15 |
| Thermal Expansion, µm/m-K | 17 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 58 to 74 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 58 to 75 | |
| 2.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 14 |
| Density, g/cm3 | 8.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 2.9 |
| Embodied Energy, MJ/kg | 41 | |
| 42 |
| Embodied Water, L/kg | 310 | |
| 140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 10 to 98 | |
| 110 to 260 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 42 to 1120 | |
| 170 to 830 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 14 |
| Stiffness to Weight: Bending, points | 18 | |
| 25 |
| Strength to Weight: Axial, points | 8.8 to 17 | |
| 26 to 32 |
| Strength to Weight: Bending, points | 11 to 16 | |
| 23 to 27 |
| Thermal Diffusivity, mm2/s | 69 | |
| 4.0 |
| Thermal Shock Resistance, points | 10 to 19 | |
| 15 to 18 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0.050 to 0.15 |
| Chromium (Cr), % | 0 | |
| 16 to 19 |
| Copper (Cu), % | 98.5 to 99.19 | |
| 0 |
| Iron (Fe), % | 0.8 to 1.2 | |
| 66.4 to 78 |
| Lead (Pb), % | 0 to 0.030 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.8 |
| Nickel (Ni), % | 0 | |
| 6.0 to 9.5 |
| Nitrogen (N), % | 0 | |
| 0 to 0.1 |
| Phosphorus (P), % | 0.010 to 0.040 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 | |
| 0 to 2.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 |
| Residuals, % | 0 to 0.2 | |
| 0 |