C19200 Copper vs. C19400 Copper
Both C19200 copper and C19400 copper are copper alloys. They have a very high 99% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C19200 copper and the bottom bar is C19400 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Elongation at Break, % | 2.0 to 35 | |
| 2.3 to 37 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 44 | |
| 44 |
| Shear Strength, MPa | 190 to 300 | |
| 210 to 300 |
| Tensile Strength: Ultimate (UTS), MPa | 280 to 530 | |
| 310 to 630 |
| Tensile Strength: Yield (Proof), MPa | 98 to 510 | |
| 98 to 520 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 200 |
| Melting Completion (Liquidus), °C | 1080 | |
| 1090 |
| Melting Onset (Solidus), °C | 1080 | |
| 1080 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 240 | |
| 260 |
| Thermal Expansion, µm/m-K | 17 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 58 to 74 | |
| 58 to 68 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 58 to 75 | |
| 58 to 69 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 30 |
| Density, g/cm3 | 8.9 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 2.6 |
| Embodied Energy, MJ/kg | 41 | |
| 40 |
| Embodied Water, L/kg | 310 | |
| 300 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 10 to 98 | |
| 5.5 to 220 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 42 to 1120 | |
| 41 to 1140 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 8.8 to 17 | |
| 9.7 to 20 |
| Strength to Weight: Bending, points | 11 to 16 | |
| 11 to 18 |
| Thermal Diffusivity, mm2/s | 69 | |
| 75 |
| Thermal Shock Resistance, points | 10 to 19 | |
| 11 to 22 |
Alloy Composition
| Copper (Cu), % | 98.5 to 99.19 | |
| 96.8 to 97.8 |
| Iron (Fe), % | 0.8 to 1.2 | |
| 2.1 to 2.6 |
| Lead (Pb), % | 0 to 0.030 | |
| 0 to 0.030 |
| Phosphorus (P), % | 0.010 to 0.040 | |
| 0.015 to 0.15 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0.050 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.2 |