C19200 Copper vs. N06219 Nickel

C19200 copper belongs to the copper alloys classification, while N06219 nickel belongs to the nickel alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is C19200 copper and the bottom bar is N06219 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
200
Elongation at Break, % 2.0 to 35
48
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 44
79
Shear Strength, MPa 190 to 300
520
Tensile Strength: Ultimate (UTS), MPa 280 to 530
730
Tensile Strength: Yield (Proof), MPa 98 to 510
300

Thermal Properties

Latent Heat of Fusion, J/g 210
330
Maximum Temperature: Mechanical, °C 200
980
Melting Completion (Liquidus), °C 1080
1430
Melting Onset (Solidus), °C 1080
1380
Specific Heat Capacity, J/kg-K 390
450
Thermal Conductivity, W/m-K 240
10
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 58 to 74
1.3
Electrical Conductivity: Equal Weight (Specific), % IACS 58 to 75
1.4

Otherwise Unclassified Properties

Base Metal Price, % relative 30
60
Density, g/cm3 8.9
8.5
Embodied Carbon, kg CO2/kg material 2.6
11
Embodied Energy, MJ/kg 41
140
Embodied Water, L/kg 310
290

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 10 to 98
280
Resilience: Unit (Modulus of Resilience), kJ/m3 42 to 1120
230
Stiffness to Weight: Axial, points 7.2
13
Stiffness to Weight: Bending, points 18
23
Strength to Weight: Axial, points 8.8 to 17
24
Strength to Weight: Bending, points 11 to 16
21
Thermal Diffusivity, mm2/s 69
2.7
Thermal Shock Resistance, points 10 to 19
21

Alloy Composition

Aluminum (Al), % 0
0 to 0.5
Carbon (C), % 0
0 to 0.050
Chromium (Cr), % 0
18 to 22
Cobalt (Co), % 0
0 to 1.0
Copper (Cu), % 98.5 to 99.19
0 to 0.5
Iron (Fe), % 0.8 to 1.2
2.0 to 4.0
Lead (Pb), % 0 to 0.030
0
Manganese (Mn), % 0
0 to 0.5
Molybdenum (Mo), % 0
7.0 to 9.0
Nickel (Ni), % 0
60.8 to 72.3
Phosphorus (P), % 0.010 to 0.040
0 to 0.020
Silicon (Si), % 0
0.7 to 1.1
Sulfur (S), % 0
0 to 0.010
Titanium (Ti), % 0
0 to 0.5
Zinc (Zn), % 0 to 0.2
0
Residuals, % 0 to 0.2
0