C19400 Copper vs. Grade Ti-Pd16 Titanium
C19400 copper belongs to the copper alloys classification, while grade Ti-Pd16 titanium belongs to the titanium alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C19400 copper and the bottom bar is grade Ti-Pd16 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Elongation at Break, % | 2.3 to 37 | |
| 17 |
| Poisson's Ratio | 0.34 | |
| 0.32 |
| Shear Modulus, GPa | 44 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 310 to 630 | |
| 390 |
| Tensile Strength: Yield (Proof), MPa | 98 to 520 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 420 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 320 |
| Melting Completion (Liquidus), °C | 1090 | |
| 1660 |
| Melting Onset (Solidus), °C | 1080 | |
| 1610 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 540 |
| Thermal Conductivity, W/m-K | 260 | |
| 22 |
| Thermal Expansion, µm/m-K | 17 | |
| 8.7 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 58 to 68 | |
| 3.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 58 to 69 | |
| 7.1 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.9 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 36 |
| Embodied Energy, MJ/kg | 40 | |
| 600 |
| Embodied Water, L/kg | 300 | |
| 230 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 5.5 to 220 | |
| 62 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 41 to 1140 | |
| 440 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 35 |
| Strength to Weight: Axial, points | 9.7 to 20 | |
| 24 |
| Strength to Weight: Bending, points | 11 to 18 | |
| 26 |
| Thermal Diffusivity, mm2/s | 75 | |
| 8.9 |
| Thermal Shock Resistance, points | 11 to 22 | |
| 30 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 96.8 to 97.8 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 2.1 to 2.6 | |
| 0 to 0.3 |
| Lead (Pb), % | 0 to 0.030 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.18 |
| Palladium (Pd), % | 0 | |
| 0.040 to 0.080 |
| Phosphorus (P), % | 0.015 to 0.15 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 98.8 to 99.96 |
| Zinc (Zn), % | 0.050 to 0.2 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |