C19500 Copper vs. AISI 334 Stainless Steel

C19500 copper belongs to the copper alloys classification, while AISI 334 stainless steel belongs to the iron alloys. There are 26 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is C19500 copper and the bottom bar is AISI 334 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
200
Elongation at Break, % 2.3 to 38
34
Poisson's Ratio 0.34
0.28
Rockwell B Hardness 71 to 86
79
Shear Modulus, GPa 44
77
Shear Strength, MPa 260 to 360
360
Tensile Strength: Ultimate (UTS), MPa 380 to 640
540
Tensile Strength: Yield (Proof), MPa 120 to 600
190

Thermal Properties

Latent Heat of Fusion, J/g 210
290
Maximum Temperature: Mechanical, °C 200
1000
Melting Completion (Liquidus), °C 1090
1410
Melting Onset (Solidus), °C 1090
1370
Specific Heat Capacity, J/kg-K 390
480
Thermal Expansion, µm/m-K 17
16

Otherwise Unclassified Properties

Base Metal Price, % relative 31
22
Density, g/cm3 8.9
7.9
Embodied Carbon, kg CO2/kg material 2.7
4.1
Embodied Energy, MJ/kg 42
59
Embodied Water, L/kg 310
170

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 14 to 110
140
Resilience: Unit (Modulus of Resilience), kJ/m3 59 to 1530
96
Stiffness to Weight: Axial, points 7.3
14
Stiffness to Weight: Bending, points 18
25
Strength to Weight: Axial, points 12 to 20
19
Strength to Weight: Bending, points 13 to 18
19
Thermal Shock Resistance, points 13 to 23
12

Alloy Composition

Aluminum (Al), % 0 to 0.020
0.15 to 0.6
Carbon (C), % 0
0 to 0.080
Chromium (Cr), % 0
18 to 20
Cobalt (Co), % 0.3 to 1.3
0
Copper (Cu), % 94.9 to 98.6
0
Iron (Fe), % 1.0 to 2.0
55.7 to 62.7
Lead (Pb), % 0 to 0.020
0
Manganese (Mn), % 0
0 to 1.0
Nickel (Ni), % 0
19 to 21
Phosphorus (P), % 0.010 to 0.35
0 to 0.030
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.015
Tin (Sn), % 0.1 to 1.0
0
Titanium (Ti), % 0
0.15 to 0.6
Zinc (Zn), % 0 to 0.2
0
Residuals, % 0 to 0.2
0