C19500 Copper vs. C33500 Brass
Both C19500 copper and C33500 brass are copper alloys. They have 64% of their average alloy composition in common.
For each property being compared, the top bar is C19500 copper and the bottom bar is C33500 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 100 |
| Elongation at Break, % | 2.3 to 38 | |
| 3.0 to 28 |
| Poisson's Ratio | 0.34 | |
| 0.31 |
| Rockwell B Hardness | 71 to 86 | |
| 53 to 91 |
| Rockwell Superficial 30T Hardness | 66 to 76 | |
| 52 to 78 |
| Shear Modulus, GPa | 44 | |
| 40 |
| Shear Strength, MPa | 260 to 360 | |
| 220 to 360 |
| Tensile Strength: Ultimate (UTS), MPa | 380 to 640 | |
| 340 to 650 |
| Tensile Strength: Yield (Proof), MPa | 120 to 600 | |
| 120 to 420 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 120 |
| Melting Completion (Liquidus), °C | 1090 | |
| 930 |
| Melting Onset (Solidus), °C | 1090 | |
| 900 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 200 | |
| 120 |
| Thermal Expansion, µm/m-K | 17 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 50 to 56 | |
| 26 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 50 to 57 | |
| 29 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 24 |
| Density, g/cm3 | 8.9 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.7 |
| Embodied Energy, MJ/kg | 42 | |
| 45 |
| Embodied Water, L/kg | 310 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 14 to 110 | |
| 8.0 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 59 to 1530 | |
| 69 to 860 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 12 to 20 | |
| 12 to 22 |
| Strength to Weight: Bending, points | 13 to 18 | |
| 13 to 21 |
| Thermal Diffusivity, mm2/s | 58 | |
| 37 |
| Thermal Shock Resistance, points | 13 to 23 | |
| 11 to 22 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.020 | |
| 0 |
| Cobalt (Co), % | 0.3 to 1.3 | |
| 0 |
| Copper (Cu), % | 94.9 to 98.6 | |
| 62 to 65 |
| Iron (Fe), % | 1.0 to 2.0 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 to 0.020 | |
| 0.25 to 0.7 |
| Phosphorus (P), % | 0.010 to 0.35 | |
| 0 |
| Tin (Sn), % | 0.1 to 1.0 | |
| 0 |
| Zinc (Zn), % | 0 to 0.2 | |
| 33.8 to 37.8 |
| Residuals, % | 0 | |
| 0 to 0.4 |