C19500 Copper vs. C78200 Nickel Silver
Both C19500 copper and C78200 nickel silver are copper alloys. They have 65% of their average alloy composition in common.
For each property being compared, the top bar is C19500 copper and the bottom bar is C78200 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Elongation at Break, % | 2.3 to 38 | |
| 3.0 to 40 |
| Poisson's Ratio | 0.34 | |
| 0.32 |
| Rockwell B Hardness | 71 to 86 | |
| 65 to 90 |
| Rockwell Superficial 30T Hardness | 66 to 76 | |
| 63 to 75 |
| Shear Modulus, GPa | 44 | |
| 43 |
| Shear Strength, MPa | 260 to 360 | |
| 280 to 400 |
| Tensile Strength: Ultimate (UTS), MPa | 380 to 640 | |
| 370 to 630 |
| Tensile Strength: Yield (Proof), MPa | 120 to 600 | |
| 170 to 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 160 |
| Melting Completion (Liquidus), °C | 1090 | |
| 1000 |
| Melting Onset (Solidus), °C | 1090 | |
| 970 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 200 | |
| 48 |
| Thermal Expansion, µm/m-K | 17 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 50 to 56 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 50 to 57 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 28 |
| Density, g/cm3 | 8.9 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 3.3 |
| Embodied Energy, MJ/kg | 42 | |
| 52 |
| Embodied Water, L/kg | 310 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 14 to 110 | |
| 18 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 59 to 1530 | |
| 130 to 1440 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 12 to 20 | |
| 12 to 21 |
| Strength to Weight: Bending, points | 13 to 18 | |
| 14 to 19 |
| Thermal Diffusivity, mm2/s | 58 | |
| 15 |
| Thermal Shock Resistance, points | 13 to 23 | |
| 12 to 21 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.020 | |
| 0 |
| Cobalt (Co), % | 0.3 to 1.3 | |
| 0 |
| Copper (Cu), % | 94.9 to 98.6 | |
| 63 to 67 |
| Iron (Fe), % | 1.0 to 2.0 | |
| 0 to 0.35 |
| Lead (Pb), % | 0 to 0.020 | |
| 1.5 to 2.5 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 | |
| 7.0 to 9.0 |
| Phosphorus (P), % | 0.010 to 0.35 | |
| 0 |
| Tin (Sn), % | 0.1 to 1.0 | |
| 0 |
| Zinc (Zn), % | 0 to 0.2 | |
| 20.2 to 28.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |