C19800 Copper vs. EN 1.8153 Steel
C19800 copper belongs to the copper alloys classification, while EN 1.8153 steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C19800 copper and the bottom bar is EN 1.8153 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 43 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 430 to 550 | |
| 670 to 2040 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 410 |
| Melting Completion (Liquidus), °C | 1070 | |
| 1440 |
| Melting Onset (Solidus), °C | 1050 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 480 |
| Thermal Conductivity, W/m-K | 260 | |
| 45 |
| Thermal Expansion, µm/m-K | 18 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 61 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 62 | |
| 8.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 2.1 |
| Density, g/cm3 | 8.9 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 1.8 |
| Embodied Energy, MJ/kg | 43 | |
| 25 |
| Embodied Water, L/kg | 320 | |
| 48 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 18 | |
| 25 |
| Strength to Weight: Axial, points | 14 to 17 | |
| 24 to 74 |
| Strength to Weight: Bending, points | 14 to 17 | |
| 22 to 46 |
| Thermal Diffusivity, mm2/s | 75 | |
| 12 |
| Thermal Shock Resistance, points | 15 to 20 | |
| 20 to 62 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0.56 to 0.64 |
| Chromium (Cr), % | 0 | |
| 0.2 to 0.4 |
| Copper (Cu), % | 95.7 to 99.47 | |
| 0 |
| Iron (Fe), % | 0.020 to 0.5 | |
| 95.7 to 96.9 |
| Magnesium (Mg), % | 0.1 to 1.0 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.7 to 1.0 |
| Phosphorus (P), % | 0.010 to 0.1 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 | |
| 1.5 to 2.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.025 |
| Tin (Sn), % | 0.1 to 1.0 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0.1 to 0.2 |
| Zinc (Zn), % | 0.3 to 1.5 | |
| 0 |
| Residuals, % | 0 to 0.2 | |
| 0 |