C21000 Brass vs. N07041 Nickel
C21000 brass belongs to the copper alloys classification, while N07041 nickel belongs to the nickel alloys. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is C21000 brass and the bottom bar is N07041 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 220 |
| Elongation at Break, % | 2.9 to 50 | |
| 14 |
| Shear Strength, MPa | 180 to 280 | |
| 850 |
| Tensile Strength: Ultimate (UTS), MPa | 240 to 450 | |
| 1400 |
| Tensile Strength: Yield (Proof), MPa | 69 to 440 | |
| 1050 |
Thermal Properties
| Melting Onset (Solidus), °C | 1050 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 450 |
| Thermal Conductivity, W/m-K | 230 | |
| 11 |
| Thermal Expansion, µm/m-K | 18 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.8 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 13 to 100 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 21 to 830 | |
| 2510 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 15 |
| Stiffness to Weight: Bending, points | 18 | |
| 25 |
| Strength to Weight: Axial, points | 7.4 to 14 | |
| 47 |
| Strength to Weight: Bending, points | 9.6 to 15 | |
| 34 |
| Thermal Diffusivity, mm2/s | 69 | |
| 3.0 |
| Thermal Shock Resistance, points | 8.1 to 15 | |
| 38 |