C22600 Bronze vs. AISI 440A Stainless Steel
C22600 bronze belongs to the copper alloys classification, while AISI 440A stainless steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C22600 bronze and the bottom bar is AISI 440A stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 200 |
| Elongation at Break, % | 2.5 to 33 | |
| 5.0 to 20 |
| Poisson's Ratio | 0.33 | |
| 0.28 |
| Shear Modulus, GPa | 42 | |
| 77 |
| Shear Strength, MPa | 220 to 320 | |
| 450 to 1040 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 570 | |
| 730 to 1790 |
| Tensile Strength: Yield (Proof), MPa | 270 to 490 | |
| 420 to 1650 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 760 |
| Melting Completion (Liquidus), °C | 1040 | |
| 1480 |
| Melting Onset (Solidus), °C | 1000 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 480 |
| Thermal Conductivity, W/m-K | 170 | |
| 23 |
| Thermal Expansion, µm/m-K | 18 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 40 | |
| 2.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 42 | |
| 2.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 9.0 |
| Density, g/cm3 | 8.7 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 2.2 |
| Embodied Energy, MJ/kg | 42 | |
| 31 |
| Embodied Water, L/kg | 310 | |
| 120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 14 to 100 | |
| 87 to 120 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 14 |
| Stiffness to Weight: Bending, points | 19 | |
| 25 |
| Strength to Weight: Axial, points | 11 to 18 | |
| 26 to 65 |
| Strength to Weight: Bending, points | 12 to 18 | |
| 23 to 43 |
| Thermal Diffusivity, mm2/s | 52 | |
| 6.2 |
| Thermal Shock Resistance, points | 11 to 19 | |
| 26 to 65 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0.6 to 0.75 |
| Chromium (Cr), % | 0 | |
| 16 to 18 |
| Copper (Cu), % | 86 to 89 | |
| 0 |
| Iron (Fe), % | 0 to 0.050 | |
| 78.4 to 83.4 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.75 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Zinc (Zn), % | 10.7 to 14 | |
| 0 |
| Residuals, % | 0 to 0.2 | |
| 0 |