C23000 Brass vs. C75400 Nickel Silver
Both C23000 brass and C75400 nickel silver are copper alloys. They have 80% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C23000 brass and the bottom bar is C75400 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Elongation at Break, % | 2.9 to 47 | |
| 2.0 to 43 |
| Poisson's Ratio | 0.33 | |
| 0.32 |
| Rockwell B Hardness | 48 to 87 | |
| 60 to 90 |
| Rockwell Superficial 30T Hardness | 51 to 77 | |
| 27 to 77 |
| Shear Modulus, GPa | 42 | |
| 46 |
| Shear Strength, MPa | 220 to 340 | |
| 250 to 370 |
| Tensile Strength: Ultimate (UTS), MPa | 280 to 590 | |
| 370 to 630 |
| Tensile Strength: Yield (Proof), MPa | 83 to 480 | |
| 130 to 590 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 190 |
| Melting Completion (Liquidus), °C | 1030 | |
| 1080 |
| Melting Onset (Solidus), °C | 990 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 160 | |
| 36 |
| Thermal Expansion, µm/m-K | 19 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 37 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 39 | |
| 7.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 32 |
| Density, g/cm3 | 8.6 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 3.8 |
| Embodied Energy, MJ/kg | 43 | |
| 59 |
| Embodied Water, L/kg | 310 | |
| 300 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 6.2 to 260 | |
| 12 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 31 to 1040 | |
| 75 to 1450 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.9 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 8.9 to 19 | |
| 12 to 21 |
| Strength to Weight: Bending, points | 11 to 18 | |
| 13 to 19 |
| Thermal Diffusivity, mm2/s | 48 | |
| 11 |
| Thermal Shock Resistance, points | 9.4 to 20 | |
| 12 to 21 |
Alloy Composition
| Copper (Cu), % | 84 to 86 | |
| 63.5 to 66.5 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.1 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 | |
| 14 to 16 |
| Zinc (Zn), % | 13.7 to 16 | |
| 16.2 to 22.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |