C23000 Brass vs. R05240 Alloy

C23000 brass belongs to the copper alloys classification, while R05240 alloy belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is C23000 brass and the bottom bar is R05240 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
150
Elongation at Break, % 2.9 to 47
25
Poisson's Ratio 0.33
0.36
Shear Modulus, GPa 42
57
Tensile Strength: Ultimate (UTS), MPa 280 to 590
270
Tensile Strength: Yield (Proof), MPa 83 to 480
170

Thermal Properties

Latent Heat of Fusion, J/g 190
210
Specific Heat Capacity, J/kg-K 390
190
Thermal Expansion, µm/m-K 19
6.8

Otherwise Unclassified Properties

Density, g/cm3 8.6
14
Embodied Water, L/kg 310
460

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 6.2 to 260
59
Resilience: Unit (Modulus of Resilience), kJ/m3 31 to 1040
90
Stiffness to Weight: Axial, points 7.2
6.3
Stiffness to Weight: Bending, points 19
13
Strength to Weight: Axial, points 8.9 to 19
5.4
Strength to Weight: Bending, points 11 to 18
6.8
Thermal Shock Resistance, points 9.4 to 20
18

Alloy Composition

Carbon (C), % 0
0 to 0.010
Copper (Cu), % 84 to 86
0
Hydrogen (H), % 0
0 to 0.0015
Iron (Fe), % 0 to 0.050
0 to 0.010
Lead (Pb), % 0 to 0.050
0
Molybdenum (Mo), % 0
0 to 0.020
Nickel (Ni), % 0
0 to 0.010
Niobium (Nb), % 0
35 to 42
Nitrogen (N), % 0
0 to 0.010
Oxygen (O), % 0
0 to 0.020
Silicon (Si), % 0
0 to 0.0050
Tantalum (Ta), % 0
57.9 to 65
Titanium (Ti), % 0
0 to 0.010
Tungsten (W), % 0
0 to 0.050
Zinc (Zn), % 13.7 to 16
0
Residuals, % 0 to 0.2
0