C23400 Brass vs. Solder Alloy 114
C23400 brass belongs to the copper alloys classification, while solder alloy 114 belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is C23400 brass and the bottom bar is solder alloy 114.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 30 |
| Poisson's Ratio | 0.32 | |
| 0.41 |
| Shear Modulus, GPa | 42 | |
| 11 |
| Tensile Strength: Ultimate (UTS), MPa | 370 to 640 | |
| 37 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 38 |
| Melting Completion (Liquidus), °C | 970 | |
| 240 |
| Melting Onset (Solidus), °C | 930 | |
| 180 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 170 |
| Thermal Conductivity, W/m-K | 120 | |
| 44 |
| Thermal Expansion, µm/m-K | 19 | |
| 26 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 27 | |
| 95 |
| Density, g/cm3 | 8.5 | |
| 9.7 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 8.3 |
| Embodied Energy, MJ/kg | 43 | |
| 140 |
| Embodied Water, L/kg | 320 | |
| 760 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 1.7 |
| Stiffness to Weight: Bending, points | 19 | |
| 11 |
| Strength to Weight: Axial, points | 12 to 21 | |
| 1.1 |
| Strength to Weight: Bending, points | 13 to 19 | |
| 2.6 |
| Thermal Diffusivity, mm2/s | 36 | |
| 27 |
| Thermal Shock Resistance, points | 12 to 22 | |
| 3.4 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.5 |
| Arsenic (As), % | 0 | |
| 0 to 0.030 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.25 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0050 |
| Copper (Cu), % | 81 to 84 | |
| 0 to 0.080 |
| Gold (Au), % | 0 | |
| 0 to 0.050 |
| Indium (In), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 to 0.020 |
| Lead (Pb), % | 0 to 0.050 | |
| 58.4 to 60.5 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Silver (Ag), % | 0 | |
| 0 to 0.1 |
| Tin (Sn), % | 0 | |
| 39.5 to 40.5 |
| Zinc (Zn), % | 15.7 to 19 | |
| 0 to 0.0010 |
| Residuals, % | 0 to 0.2 | |
| 0 |