C23400 Brass vs. C33000 Brass
Both C23400 brass and C33000 brass are copper alloys. They have 84% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is C23400 brass and the bottom bar is C33000 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Poisson's Ratio | 0.32 | |
| 0.31 |
| Rockwell Superficial 30T Hardness | 51 to 78 | |
| 26 to 69 |
| Shear Modulus, GPa | 42 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 370 to 640 | |
| 320 to 520 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 130 |
| Melting Completion (Liquidus), °C | 970 | |
| 940 |
| Melting Onset (Solidus), °C | 930 | |
| 900 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 120 | |
| 120 |
| Thermal Expansion, µm/m-K | 19 | |
| 20 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 27 | |
| 24 |
| Density, g/cm3 | 8.5 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 2.7 |
| Embodied Energy, MJ/kg | 43 | |
| 45 |
| Embodied Water, L/kg | 320 | |
| 320 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 12 to 21 | |
| 11 to 18 |
| Strength to Weight: Bending, points | 13 to 19 | |
| 13 to 18 |
| Thermal Diffusivity, mm2/s | 36 | |
| 37 |
| Thermal Shock Resistance, points | 12 to 22 | |
| 11 to 17 |
Alloy Composition
| Copper (Cu), % | 81 to 84 | |
| 65 to 68 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 to 0.070 |
| Lead (Pb), % | 0 to 0.050 | |
| 0.25 to 0.7 |
| Zinc (Zn), % | 15.7 to 19 | |
| 30.8 to 34.8 |
| Residuals, % | 0 | |
| 0 to 0.4 |