C23400 Brass vs. N08024 Nickel
C23400 brass belongs to the copper alloys classification, while N08024 nickel belongs to the nickel alloys. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is C23400 brass and the bottom bar is N08024 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 200 |
| Poisson's Ratio | 0.32 | |
| 0.28 |
| Shear Modulus, GPa | 42 | |
| 79 |
| Tensile Strength: Ultimate (UTS), MPa | 370 to 640 | |
| 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 310 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 990 |
| Melting Completion (Liquidus), °C | 970 | |
| 1430 |
| Melting Onset (Solidus), °C | 930 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 460 |
| Thermal Conductivity, W/m-K | 120 | |
| 12 |
| Thermal Expansion, µm/m-K | 19 | |
| 15 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 27 | |
| 41 |
| Density, g/cm3 | 8.5 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 7.2 |
| Embodied Energy, MJ/kg | 43 | |
| 99 |
| Embodied Water, L/kg | 320 | |
| 230 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 14 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 12 to 21 | |
| 21 |
| Strength to Weight: Bending, points | 13 to 19 | |
| 20 |
| Thermal Diffusivity, mm2/s | 36 | |
| 3.2 |
| Thermal Shock Resistance, points | 12 to 22 | |
| 15 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 | |
| 22.5 to 25 |
| Copper (Cu), % | 81 to 84 | |
| 0.5 to 1.5 |
| Iron (Fe), % | 0 to 0.050 | |
| 26.6 to 38.4 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 3.5 to 5.0 |
| Nickel (Ni), % | 0 | |
| 35 to 40 |
| Niobium (Nb), % | 0 | |
| 0.15 to 0.35 |
| Phosphorus (P), % | 0 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.035 |
| Zinc (Zn), % | 15.7 to 19 | |
| 0 |
| Residuals, % | 0 to 0.2 | |
| 0 |