C23400 Brass vs. ZK61A Magnesium
C23400 brass belongs to the copper alloys classification, while ZK61A magnesium belongs to the magnesium alloys. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is C23400 brass and the bottom bar is ZK61A magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 46 |
| Poisson's Ratio | 0.32 | |
| 0.29 |
| Shear Modulus, GPa | 42 | |
| 18 |
| Tensile Strength: Ultimate (UTS), MPa | 370 to 640 | |
| 290 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 330 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 120 |
| Melting Completion (Liquidus), °C | 970 | |
| 640 |
| Melting Onset (Solidus), °C | 930 | |
| 530 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 960 |
| Thermal Conductivity, W/m-K | 120 | |
| 120 |
| Thermal Expansion, µm/m-K | 19 | |
| 27 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 27 | |
| 13 |
| Density, g/cm3 | 8.5 | |
| 1.9 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 23 |
| Embodied Energy, MJ/kg | 43 | |
| 160 |
| Embodied Water, L/kg | 320 | |
| 940 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 62 |
| Strength to Weight: Axial, points | 12 to 21 | |
| 42 to 45 |
| Strength to Weight: Bending, points | 13 to 19 | |
| 50 to 53 |
| Thermal Diffusivity, mm2/s | 36 | |
| 65 |
| Thermal Shock Resistance, points | 12 to 22 | |
| 17 to 18 |
Alloy Composition
| Copper (Cu), % | 81 to 84 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Magnesium (Mg), % | 0 | |
| 92.1 to 93.9 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Zinc (Zn), % | 15.7 to 19 | |
| 5.5 to 6.5 |
| Zirconium (Zr), % | 0 | |
| 0.6 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.3 |