C24000 Brass vs. N06045 Nickel
C24000 brass belongs to the copper alloys classification, while N06045 nickel belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is C24000 brass and the bottom bar is N06045 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 200 |
| Poisson's Ratio | 0.32 | |
| 0.28 |
| Shear Modulus, GPa | 42 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 310 to 640 | |
| 690 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 350 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 1010 |
| Melting Completion (Liquidus), °C | 1000 | |
| 1350 |
| Melting Onset (Solidus), °C | 970 | |
| 1300 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 480 |
| Thermal Expansion, µm/m-K | 19 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 27 | |
| 42 |
| Density, g/cm3 | 8.5 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 6.9 |
| Embodied Energy, MJ/kg | 43 | |
| 98 |
| Embodied Water, L/kg | 320 | |
| 250 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 14 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 10 to 21 | |
| 24 |
| Strength to Weight: Bending, points | 12 to 20 | |
| 22 |
| Thermal Shock Resistance, points | 10 to 22 | |
| 18 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0.050 to 0.12 |
| Cerium (Ce), % | 0 | |
| 0.030 to 0.090 |
| Chromium (Cr), % | 0 | |
| 26 to 29 |
| Copper (Cu), % | 78.5 to 81.5 | |
| 0 to 0.3 |
| Iron (Fe), % | 0 to 0.050 | |
| 21 to 25 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 | |
| 45 to 50.4 |
| Phosphorus (P), % | 0 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 | |
| 2.5 to 3.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Zinc (Zn), % | 18.2 to 21.5 | |
| 0 |
| Residuals, % | 0 to 0.2 | |
| 0 |