C26000 Brass vs. EN 1.1151 Steel
C26000 brass belongs to the copper alloys classification, while EN 1.1151 steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C26000 brass and the bottom bar is EN 1.1151 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 2.5 to 66 | |
| 21 to 26 |
| Poisson's Ratio | 0.31 | |
| 0.29 |
| Shear Modulus, GPa | 41 | |
| 73 |
| Shear Strength, MPa | 230 to 390 | |
| 300 to 330 |
| Tensile Strength: Ultimate (UTS), MPa | 320 to 680 | |
| 460 to 520 |
| Tensile Strength: Yield (Proof), MPa | 110 to 570 | |
| 240 to 340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 140 | |
| 400 |
| Melting Completion (Liquidus), °C | 950 | |
| 1460 |
| Melting Onset (Solidus), °C | 920 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Conductivity, W/m-K | 120 | |
| 50 |
| Thermal Expansion, µm/m-K | 20 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 31 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 2.1 |
| Density, g/cm3 | 8.2 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 1.4 |
| Embodied Energy, MJ/kg | 45 | |
| 19 |
| Embodied Water, L/kg | 320 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 6.1 to 420 | |
| 98 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 51 to 1490 | |
| 160 to 310 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 11 to 23 | |
| 16 to 18 |
| Strength to Weight: Bending, points | 13 to 21 | |
| 17 to 18 |
| Thermal Diffusivity, mm2/s | 38 | |
| 13 |
| Thermal Shock Resistance, points | 11 to 23 | |
| 15 to 16 |
Alloy Composition
| Bismuth (Bi), % | 0 to 0.0059 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.17 to 0.24 |
| Chromium (Cr), % | 0 | |
| 0 to 0.4 |
| Copper (Cu), % | 68.5 to 71.5 | |
| 0 |
| Iron (Fe), % | 0 to 0.050 | |
| 97.7 to 99.43 |
| Lead (Pb), % | 0 to 0.070 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.4 to 0.7 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 | |
| 0 to 0.4 |
| Phosphorus (P), % | 0 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 | |
| 0 to 0.035 |
| Zinc (Zn), % | 28.1 to 31.5 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 |