C26000 Brass vs. SAE-AISI S2 Steel

C26000 brass belongs to the copper alloys classification, while SAE-AISI S2 steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is C26000 brass and the bottom bar is SAE-AISI S2 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
190
Poisson's Ratio 0.31
0.29
Shear Modulus, GPa 41
72
Tensile Strength: Ultimate (UTS), MPa 320 to 680
670 to 1940

Thermal Properties

Latent Heat of Fusion, J/g 180
260
Melting Completion (Liquidus), °C 950
1450
Melting Onset (Solidus), °C 920
1410
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 120
44
Thermal Expansion, µm/m-K 20
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 28
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 31
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 25
2.6
Density, g/cm3 8.2
7.8
Embodied Carbon, kg CO2/kg material 2.7
2.1
Embodied Energy, MJ/kg 45
30
Embodied Water, L/kg 320
49

Common Calculations

Stiffness to Weight: Axial, points 7.2
13
Stiffness to Weight: Bending, points 19
24
Strength to Weight: Axial, points 11 to 23
24 to 69
Strength to Weight: Bending, points 13 to 21
22 to 44
Thermal Diffusivity, mm2/s 38
12
Thermal Shock Resistance, points 11 to 23
23 to 68

Alloy Composition

Bismuth (Bi), % 0 to 0.0059
0
Carbon (C), % 0
0.4 to 0.55
Copper (Cu), % 68.5 to 71.5
0 to 0.25
Iron (Fe), % 0 to 0.050
96 to 98.1
Lead (Pb), % 0 to 0.070
0
Manganese (Mn), % 0
0.3 to 0.5
Molybdenum (Mo), % 0
0.3 to 0.6
Nickel (Ni), % 0
0 to 0.3
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0.9 to 1.2
Sulfur (S), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.5
Zinc (Zn), % 28.1 to 31.5
0
Residuals, % 0 to 0.3
0