C26000 Brass vs. C26800 Brass
Both C26000 brass and C26800 brass are copper alloys. They have a very high 96% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is C26000 brass and the bottom bar is C26800 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Poisson's Ratio | 0.31 | |
| 0.31 |
| Rockwell B Hardness | 53 to 93 | |
| 53 to 91 |
| Shear Modulus, GPa | 41 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 320 to 680 | |
| 310 to 650 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 140 | |
| 130 |
| Melting Completion (Liquidus), °C | 950 | |
| 930 |
| Melting Onset (Solidus), °C | 920 | |
| 900 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 120 | |
| 120 |
| Thermal Expansion, µm/m-K | 20 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 27 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 31 | |
| 30 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 24 |
| Density, g/cm3 | 8.2 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.7 |
| Embodied Energy, MJ/kg | 45 | |
| 45 |
| Embodied Water, L/kg | 320 | |
| 320 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 11 to 23 | |
| 11 to 22 |
| Strength to Weight: Bending, points | 13 to 21 | |
| 13 to 21 |
| Thermal Diffusivity, mm2/s | 38 | |
| 37 |
| Thermal Shock Resistance, points | 11 to 23 | |
| 10 to 22 |
Alloy Composition
| Bismuth (Bi), % | 0 to 0.0059 | |
| 0 |
| Copper (Cu), % | 68.5 to 71.5 | |
| 64 to 68.5 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 to 0.070 | |
| 0 to 0.15 |
| Zinc (Zn), % | 28.1 to 31.5 | |
| 31 to 36 |
| Residuals, % | 0 | |
| 0 to 0.3 |