C26000 Brass vs. C55180 Copper
Both C26000 brass and C55180 copper are copper alloys. They have 70% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C26000 brass and the bottom bar is C55180 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 2.5 to 66 | |
| 20 |
| Poisson's Ratio | 0.31 | |
| 0.34 |
| Shear Modulus, GPa | 41 | |
| 41 |
| Tensile Strength: Ultimate (UTS), MPa | 320 to 680 | |
| 200 |
| Tensile Strength: Yield (Proof), MPa | 110 to 570 | |
| 100 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 140 | |
| 200 |
| Melting Completion (Liquidus), °C | 950 | |
| 920 |
| Melting Onset (Solidus), °C | 920 | |
| 710 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 400 |
| Thermal Conductivity, W/m-K | 120 | |
| 200 |
| Thermal Expansion, µm/m-K | 20 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 29 |
| Density, g/cm3 | 8.2 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.5 |
| Embodied Energy, MJ/kg | 45 | |
| 39 |
| Embodied Water, L/kg | 320 | |
| 290 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 6.1 to 420 | |
| 34 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 51 to 1490 | |
| 48 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 11 to 23 | |
| 6.4 |
| Strength to Weight: Bending, points | 13 to 21 | |
| 8.8 |
| Thermal Diffusivity, mm2/s | 38 | |
| 56 |
| Thermal Shock Resistance, points | 11 to 23 | |
| 7.9 |
Alloy Composition
| Bismuth (Bi), % | 0 to 0.0059 | |
| 0 |
| Copper (Cu), % | 68.5 to 71.5 | |
| 94.7 to 95.2 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 |
| Lead (Pb), % | 0 to 0.070 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 4.8 to 5.2 |
| Zinc (Zn), % | 28.1 to 31.5 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.15 |