C26200 Brass vs. EN 1.7201 Steel
C26200 brass belongs to the copper alloys classification, while EN 1.7201 steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is C26200 brass and the bottom bar is EN 1.7201 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Poisson's Ratio | 0.31 | |
| 0.29 |
| Shear Modulus, GPa | 41 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 770 | |
| 430 to 1300 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 140 | |
| 420 |
| Melting Completion (Liquidus), °C | 950 | |
| 1460 |
| Melting Onset (Solidus), °C | 920 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Conductivity, W/m-K | 120 | |
| 45 |
| Thermal Expansion, µm/m-K | 20 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 31 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 2.5 |
| Density, g/cm3 | 8.2 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 1.5 |
| Embodied Energy, MJ/kg | 45 | |
| 20 |
| Embodied Water, L/kg | 320 | |
| 51 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 11 to 26 | |
| 15 to 46 |
| Strength to Weight: Bending, points | 13 to 23 | |
| 16 to 34 |
| Thermal Diffusivity, mm2/s | 38 | |
| 12 |
| Thermal Shock Resistance, points | 11 to 26 | |
| 13 to 38 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0.1 to 0.15 |
| Chromium (Cr), % | 0 | |
| 0.9 to 1.2 |
| Copper (Cu), % | 67 to 70 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 0.050 | |
| 96.9 to 98.3 |
| Lead (Pb), % | 0 to 0.070 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.6 to 0.9 |
| Molybdenum (Mo), % | 0 | |
| 0.15 to 0.25 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 | |
| 0 to 0.025 |
| Zinc (Zn), % | 29.6 to 33 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 |