C26200 Brass vs. Z13004 Zinc
C26200 brass belongs to the copper alloys classification, while Z13004 zinc belongs to the zinc alloys. They have a modest 31% of their average alloy composition in common, which, by itself, doesn't mean much. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C26200 brass and the bottom bar is Z13004 zinc.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 87 |
| Elongation at Break, % | 3.0 to 180 | |
| 30 |
| Poisson's Ratio | 0.31 | |
| 0.25 |
| Shear Modulus, GPa | 41 | |
| 35 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 770 | |
| 93 |
| Tensile Strength: Yield (Proof), MPa | 110 to 490 | |
| 76 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 110 |
| Maximum Temperature: Mechanical, °C | 140 | |
| 90 |
| Melting Completion (Liquidus), °C | 950 | |
| 410 |
| Melting Onset (Solidus), °C | 920 | |
| 390 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 120 | |
| 110 |
| Thermal Expansion, µm/m-K | 20 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 27 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 31 | |
| 37 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 11 |
| Density, g/cm3 | 8.2 | |
| 6.6 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.8 |
| Embodied Energy, MJ/kg | 45 | |
| 53 |
| Embodied Water, L/kg | 320 | |
| 340 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 19 to 160 | |
| 26 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 62 to 1110 | |
| 33 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 19 | |
| 23 |
| Strength to Weight: Axial, points | 11 to 26 | |
| 3.9 |
| Strength to Weight: Bending, points | 13 to 23 | |
| 7.0 |
| Thermal Diffusivity, mm2/s | 38 | |
| 44 |
| Thermal Shock Resistance, points | 11 to 26 | |
| 2.9 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0020 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0030 |
| Copper (Cu), % | 67 to 70 | |
| 0 to 0.0030 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 to 0.0030 |
| Lead (Pb), % | 0 to 0.070 | |
| 0 to 0.0030 |
| Tin (Sn), % | 0 | |
| 0 to 0.0010 |
| Zinc (Zn), % | 29.6 to 33 | |
| 99.985 to 100 |
| Residuals, % | 0 to 0.3 | |
| 0 |