C26200 Brass vs. R30003 Cobalt
C26200 brass belongs to the copper alloys classification, while R30003 cobalt belongs to the cobalt alloys. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C26200 brass and the bottom bar is R30003 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 210 |
| Elongation at Break, % | 3.0 to 180 | |
| 10 to 73 |
| Poisson's Ratio | 0.31 | |
| 0.29 |
| Shear Modulus, GPa | 41 | |
| 83 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 770 | |
| 970 to 1720 |
| Tensile Strength: Yield (Proof), MPa | 110 to 490 | |
| 510 to 1090 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 310 |
| Melting Completion (Liquidus), °C | 950 | |
| 1400 |
| Melting Onset (Solidus), °C | 920 | |
| 1440 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 450 |
| Thermal Conductivity, W/m-K | 120 | |
| 13 |
| Thermal Expansion, µm/m-K | 20 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 2.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 31 | |
| 2.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 95 |
| Density, g/cm3 | 8.2 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 8.0 |
| Embodied Energy, MJ/kg | 45 | |
| 110 |
| Embodied Water, L/kg | 320 | |
| 400 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 62 to 1110 | |
| 600 to 2790 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 14 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 11 to 26 | |
| 32 to 57 |
| Strength to Weight: Bending, points | 13 to 23 | |
| 26 to 38 |
| Thermal Diffusivity, mm2/s | 38 | |
| 3.3 |
| Thermal Shock Resistance, points | 11 to 26 | |
| 26 to 45 |
Alloy Composition
| Boron (B), % | 0 | |
| 0 to 0.1 |
| Carbon (C), % | 0 | |
| 0 to 0.15 |
| Chromium (Cr), % | 0 | |
| 19 to 21 |
| Cobalt (Co), % | 0 | |
| 39 to 41 |
| Copper (Cu), % | 67 to 70 | |
| 0 |
| Iron (Fe), % | 0 to 0.050 | |
| 10 to 20.5 |
| Lead (Pb), % | 0 to 0.070 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 1.5 to 2.5 |
| Molybdenum (Mo), % | 0 | |
| 6.0 to 8.0 |
| Nickel (Ni), % | 0 | |
| 14 to 16 |
| Phosphorus (P), % | 0 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 | |
| 0 to 1.2 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Zinc (Zn), % | 29.6 to 33 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 |