C27400 Brass vs. C75200 Nickel Silver
Both C27400 brass and C75200 nickel silver are copper alloys. They have 79% of their average alloy composition in common.
For each property being compared, the top bar is C27400 brass and the bottom bar is C75200 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Poisson's Ratio | 0.31 | |
| 0.32 |
| Rockwell B Hardness | 53 to 91 | |
| 63 to 93 |
| Rockwell Superficial 30T Hardness | 52 to 78 | |
| 58 to 78 |
| Shear Modulus, GPa | 40 | |
| 47 |
| Tensile Strength: Ultimate (UTS), MPa | 370 to 650 | |
| 400 to 660 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 200 |
| Melting Completion (Liquidus), °C | 920 | |
| 1110 |
| Melting Onset (Solidus), °C | 870 | |
| 1070 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 400 |
| Thermal Conductivity, W/m-K | 120 | |
| 33 |
| Thermal Expansion, µm/m-K | 21 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 6.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 31 | |
| 6.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 33 |
| Density, g/cm3 | 8.0 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 4.1 |
| Embodied Energy, MJ/kg | 45 | |
| 62 |
| Embodied Water, L/kg | 320 | |
| 300 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.2 | |
| 8.0 |
| Stiffness to Weight: Bending, points | 20 | |
| 19 |
| Strength to Weight: Axial, points | 13 to 23 | |
| 13 to 21 |
| Strength to Weight: Bending, points | 14 to 21 | |
| 14 to 20 |
| Thermal Diffusivity, mm2/s | 37 | |
| 9.8 |
| Thermal Shock Resistance, points | 12 to 22 | |
| 13 to 22 |
Alloy Composition
| Copper (Cu), % | 61 to 64 | |
| 63.5 to 66.5 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 | |
| 16.5 to 19.5 |
| Zinc (Zn), % | 35.6 to 39 | |
| 12.7 to 20 |
| Residuals, % | 0 | |
| 0 to 0.5 |